Fission-fusion correlation by fission reactor irradiation with improved control
- 2 November 1990
- journal article
- Published by Elsevier in Journal of Nuclear Materials
- Vol. 174 (2-3) , 327-351
- https://doi.org/10.1016/0022-3115(90)90245-i
Abstract
No abstract availableKeywords
This publication has 13 references indexed in Scilit:
- The Concept of Production Bias and Its Possible Role in Defect Accumulation under Cascade Damage ConditionsPhysica Status Solidi (b), 1990
- Radiation rate dependence of microstructure evolutionJournal of Nuclear Materials, 1989
- Correlation of interstitials within defect cascades in Al(Zn) and Cu observed by diffuse X-Ray scatteringJournal of Nuclear Materials, 1989
- The need for improved temperature control during reactor irradiationJournal of Nuclear Materials, 1988
- Defect structure development in 14 mev neutron irradiated copper and copper dilute alloysJournal of Nuclear Materials, 1988
- Defect structure evolution from cascade damage in 14 Mev neutron irradiated nickel and nickel alloysJournal of Nuclear Materials, 1988
- Detection and analysis of microscopically invisible cascade defects in 14 MeV neutron irradiated aluminum and ironJournal of Nuclear Materials, 1988
- Recoil energy effects and defect processes in neutron irradiated metalsJournal of Nuclear Materials, 1988
- Development of defects from displacement cascade damage in low temperature D-T neutron-irradiated metalsJournal of Nuclear Materials, 1986
- Factors controlling the nature and amount of residual defects in neutron irradiated materialsJournal of Nuclear Materials, 1986