Impurity effects in tungsten phosphate glasses. II. Electrical and optical properties

Publisher Website
Google Scholar
Abstract
For pt.I see ibid., vol.6, no.24, 3661 (1973). The electrical and optical properties of semiconducting glasses made from 67 MOL% WO3:33 mol% P2O5 and 0.2-8.6 mol% V2O5, MoO3 or CuO have been investigated. V2O5 and MoO3 reduce the conductivity sharply while CuO and most other transition metal oxides have little effect. The dominant parameter is the activation energy for conduction which varies inversely as impurity spacing at low impurity concentrations. Isolated impurity ions induce localization energies of about 0.75 eV for V ions and 0.80 eV for Mo ions. In the case of vanadium, interaction effects reduce these energies eventually resulting in direct electron hopping between impurity sites. The results may be related to properties of V2O5:P2O5 glasses. Thermopower and optical absorption measurements on undoped glasses are consistent with a small-polaron hopping mechanism, and the correlation Wopt approximately 4 WH, where Wopt is the energy of the absorption peak, is qualitatively observed even for doped glasses. However, the conduction process cannot be described in terms of a simple form of trap-controlled drift mobility, and a model involving electrostatic interactions between impurity sites appears to be necessary.

This publication has 21 references indexed in Scilit: