Neutron Diffraction Study on Preferred Orientation of Ag-Sheathed Y-Ba-Cu-O Superconductor Tape with Jc=1000–3000 A/cm2
- 1 September 1988
- journal article
- Published by IOP Publishing in Japanese Journal of Applied Physics
- Vol. 27 (9A) , L1715
- https://doi.org/10.1143/jjap.27.l1715
Abstract
Ag-sheathed tapes using tetragonal phase of YBa2Cu3O x were fabricated by cold rolling. Neutron diffraction study was undertaken to investigate the orientation of YBCO grains in the Ag-sheathed tape. It was clearly observed that the c-plane of crystal was aligned parallel to the cold rolling surface with a standard deviation of 26.7 degree. The preferred orientation was enhanced by using the tetragonal phase.Keywords
This publication has 11 references indexed in Scilit:
- Superconductivity at 90 K in the Tl-Ba-Cu-O systemPhysical Review Letters, 1988
- A New High-Tc Oxide Superconductor without a Rare Earth ElementJapanese Journal of Applied Physics, 1988
- Fabrication of Ag-Sheathed Ba-Y-Cu Oxide Superconductor TapeJapanese Journal of Applied Physics, 1988
- Preparation of Oriented Orthorhombic LnBa2Cu3O7-x PolycrystalsJapanese Journal of Applied Physics, 1987
- Determination of Oxygen Nonstoichiometry in a High-Tc Superconductor Ba2YCu3O7-δJapanese Journal of Applied Physics, 1987
- Structure of High-Tc Superconductor YBa2Cu3O6.6 at Low TemperaturesJapanese Journal of Applied Physics, 1987
- Anisotropy of the Upper Critical Magnetic Field in Single Crystal YBa2Cu3O7+yJapanese Journal of Applied Physics, 1987
- Critical Current Density of Wire Type Y-Ba-Cu Oxide SuperconductorJapanese Journal of Applied Physics, 1987
- Superconductivity at 93 K in a new mixed-phase Y-Ba-Cu-O compound system at ambient pressurePhysical Review Letters, 1987
- Possible highT c superconductivity in the Ba?La?Cu?O systemZeitschrift für Physik B Condensed Matter, 1986