Development of high-strength, high-conductivity Cu–Ag alloys for high-field pulsed magnet use
- 2 December 1991
- journal article
- Published by AIP Publishing in Applied Physics Letters
- Vol. 59 (23) , 2965-2967
- https://doi.org/10.1063/1.105813
Abstract
A wire‐conductor fabrication method has been developed for Cu–Ag alloys containing 2–60 at. % Ag where high strength and high conductivity conductors are obtained by cold working combined with intermediate heat treatment. The intermediate heat treatment is repeated 3–4 times at 350–450 °C for 1–2 h at appropriate stages of reduction of area. The optimized Cu‐16 at. % Ag alloy wire with 99% reduction of area showed a tensile strength of 1000 MPa and an electrical conductivity of 80% IACS at room temperature. This suggests that the wires fabricated may be very promising for high‐field pulsed magnet use.Keywords
This publication has 8 references indexed in Scilit:
- Development of deformation processed copper-refractory metal composite alloysJournal of Materials Engineering, 1990
- D.C. laboratory electromagnetsPhysica B: Condensed Matter, 1989
- Characterization of the strength and microstructure of heavily cold worked CuNb compositesActa Metallurgica, 1987
- 68.4-T-long pulse magnet: Test of high strength microcomposite Cu/Nb conductorApplied Physics Letters, 1986
- On the strength of heavily cold worked in situ compositesActa Metallurgica, 1985
- Anomalous increase in strength of i n s i t u formed Cu-Nb multifilamentary compositesJournal of Applied Physics, 1978
- Microstructure and anomalous mechanical properties of in situ-produced silver-copper composite wiresActa Metallurgica, 1975
- Precipitation Hardening in Copper-Silver AlloysJournal of the Japan Institute of Metals and Materials, 1969