Particle size, volume fraction and matrix strength effects on fatigue behavior and particle fracture in 2124 aluminum-SiCp composites
- 1 June 1994
- journal article
- Published by Elsevier in Materials Science and Engineering: A
- Vol. 183 (1-2) , 69-80
- https://doi.org/10.1016/0921-5093(94)90891-5
Abstract
No abstract availableKeywords
This publication has 38 references indexed in Scilit:
- Damage due to fracture of brittle reinforcements in a ductile matrixActa Metallurgica et Materialia, 1992
- On the fracture toughness of particulate reinforced metal-matrix compositesScripta Metallurgica et Materialia, 1991
- Stress-strain behavior of metal matrix composites with discontinuous reinforcementsScripta Metallurgica et Materialia, 1991
- Strengthening of a particulate metal matrix composite by quenchingActa Metallurgica et Materialia, 1991
- Aspects of fracture in particulate reinforced metal matrix compositesActa Metallurgica et Materialia, 1991
- Strengthening of composites due to microstructural changes in the matrixActa Metallurgica et Materialia, 1991
- Strengthening mechanisms in particulate metal matrix compositesScripta Metallurgica et Materialia, 1991
- The role of equiaxed particles on the yield stress of compositesScripta Metallurgica et Materialia, 1991
- The growth of fatigue cracks through particulate sic reinforced aluminum alloysEngineering Fracture Mechanics, 1989
- Assessment of models used to predict the strength of discontinous silicon carbide reinforced aluminum alloysScripta Metallurgica, 1987