Empirical Formulations for the Analysis and Prediction of Trends for Steady-State Fatigue Crack Growth Rates
- 1 September 1977
- journal article
- Published by ASTM International in Journal of Testing and Evaluation
- Vol. 5 (5) , 343-353
- https://doi.org/10.1520/jte10541j
Abstract
No abstract availableKeywords
This publication has 12 references indexed in Scilit:
- Comparison of several fatigue crack propagation laws with experimental resultsEngineering Fracture Mechanics, 1974
- A Test Procedure for Determining the Influence of Stress Ratio on Fatigue Crack GrowthJournal of Testing and Evaluation, 1974
- Threshold for Fatigue Crack Propagation and the Effects of Load Ratio and FrequencyPublished by ASTM International ,1973
- Environmental fatigue crack propagation of aluminum alloys at low stress intensity levelsMetallurgical Transactions, 1970
- Some aspects of environment-enhanced fatigue-crack growthEngineering Fracture Mechanics, 1970
- The influence of gaseous environment and fatigue frequency on the growth of fatigue cracks in some aluminum alloysInternational Journal of Fracture, 1969
- The effect of D2O on fatigue-crack propagation in a high-strength aluminum alloyInternational Journal of Fracture, 1969
- Fatigue-crack propagation in a high-strength aluminum alloyInternational Journal of Fracture, 1968
- Fatigue Crack Propagation in MetalsNature, 1966
- On the effect of oxygen and water vapor on the propagation of fatigue cracks in 2024-T3 alclad sheetInternational Journal of Fracture, 1965