Fabrication of thermally stable and cost-effective polymeric waveguide for optical printed-circuit board

Publisher Website
Google Scholar
Abstract
A thermally stable polymeric optical waveguide has been fabricated using ultraviolet (UV)-curable epoxy resins for the core and clad materials. A simple and cost-effective fabrication method that uses reusable polydimethylsiloxane (PDMS) masters has been developed. The 12-channel under-clad layer of the UV-cured epoxy was prepared using a PDMS master whose embossed channels had been fabricated by a polycarbonate (PC) secondary master. The thermal stability of the fabricated waveguide was tested at 200 °C for one hour. The optical waveguide was not damaged physically by thermal stress. Propagation losses detected by a cut-back method were 0.16 dB/cm and 0.26 dB/cm, respectively, before and after the thermal stability test at 850 nm. Loss increase after the thermal treatment can be attributed to the formation of the absorbing and scattering sources. This waveguide can be applied for areas that require thermal stability such as an optical printed-circuit board.