Poly(phenylenevinylene) analogs with ring substituted polar side chains and their use in the formation of hydrogen bonding basedself-assembled multilayers

Publisher Website
Google Scholar
Abstract
Poly(arylenevinylene) homopolymers and copolymers with polar hydroxy and carboxy moieties attached to the aromatic phenyl ring were prepared. The copolymers and the related homopolymers are copoly[5-(2-hydroxyethoxy)-2-methoxy-1,4-phenylenevinylene/1,4-phenylenevinylene], co(PHydroxyV-PV), and copoly(5-carboxymethoxy-2-methoxy-1,4-phenylenevinylene/1,4-phenylenevinylene), co(PCarboxyV-PV). For co(PHydroxyV-PV) the photoluminescence and electroluminescence spectra can be adjusted over a range of 100 nm as a function of the percentage of the hydroxy substituted phenyl ring. For co(PCarboxyV-PV) the observed spectral features are a function of the pH from which the final conjugated polymer was prepared. The optical density and photoluminescence of co(PCarboxyV-PV) films prepared from solutions at pH=12 were significantly blue-shifted compared to polymers prepared from pH=2 solutions at up to 30% substitution at the phenyl ring. The presence of the polar side chain was used to form self-assembled multilayer films, poly(ethyleneimine)/poly(styrenesulfonate)/co(PHydroxyV-PV), based on hydrogen bonding interactions rather than electrostatic forces. The luminescence spectra in the layered systems were blue-shifted compared to the spin coated films.

This publication has 0 references indexed in Scilit: