Solid Freeform Fabrication of Aqueous Alumina–Poly(vinyl alcohol) Gelcasting Suspensions

Publisher Website
Google Scholar
Abstract
Solid freeform fabrication of aqueous alumina–poly(vinyl alcohol) (Al2O3–PVA) gel‐casting suspensions was conducted using a computer‐controlled extrusion apparatus fitted with a two‐nozzle delivery system. The impact of casting parameters on the shear rate profiles experienced during deposition was evaluated via conventional flow analysis and computer simulations. In addition, the influence of these parameters on line resolution/uniformity, printability, and as‐cast component properties was studied using laser profilometry, optical microscopy, and scanning electron microscopy. Continuous printablity was achieved for tip diameters ranging from 0.254 to 1.370 mm for all mixing rates and suspension compositions studied. Printed lines were uniform with good edge definition, and line dimensions were independent of mixing rate for these process conditions. The Al2O3 volume fraction (φAl2O3) in the as‐deposited layers depended on casting conditions and cross‐linking agent concentration, where (φAl2O3 increased with decreased tip diameter and increased cross‐linking agent concentration. The free‐formed Al2O3 components exhibited uniform particle packing, with minimal macrodefects (e.g., slumping or staircasing) and no discernable microdefects (e.g., bubbles or cracking).