Fabric changes in consolidated kaolin

Publisher Website
Google Scholar
Abstract
Samples of a remoulded kaolin were consolidated to several pressures up to 1000 kg/cm2 (100 000 kN/m2). Specimens were prepared and examined in an electron microscope and a new method of quantitative analysis, involving the direct measurement of microstructural features, was applied to the electron micrographs over the range of pressure. Features measured were the length, breadth, and orientation of the domains, and of the voids between the domains, the domain packing density, and some aspects of inter-domain contacts. The fabric changes accompanying consolidation are described. The void ratio curve exhibited two stages of consolidation, the change occurring at a pressure of approximately 0·15 kg/cm2 (14·7 kN/m2). Many of the measured features showed similar patterns of variation. This is attributed to the rupture of inter-domain (and inter-particle) physico-chemical bonds at about this pressure. On a consolidé des échantillons de kaolin remaniés, sous différenes pressions allant jusqua'à 1000 kg/cm2 (100 000 kN/m2). On a préparé et examiné ces échantillons au microscope électronique et on a utilisé une nouvelle méthoded'analyse quantitative, mettant en jeu la mesure directe des microstructures pour l'étude des microphotographies électroniques couvrant le domaine de pression étudié. Les caractéristiques mesurées sont: la longueur, la largeur et l'orientation des particules, et des vides entre et l'orientation des particules, et des vides entre les domaines, la densité d'empilemet des particules, et quelques autres aspects des contacts entre les particules. On décrit les changemet de structure qui se produisent par consolidation. La courbe de l'indice des vides démontre qu'il y a deux étapes dans la consolidation, le changement se produisant à une pression d'environ 0·15kg/cm2 (14·7 kN/m2). Un grand nombre de caractéristiques structurales suivent un schéma de variation similaire. On attribue ceci à la rupture des liaisons physicochimiques entre particules autour de cette pression. Samples of a remoulded kaolin were consolidated to several pressures up to 1000 kg/cm2 (100 000 kN/m2). Specimens were prepared and examined in an electron microscope and a new method of quantitative analysis, involving the direct measurement of microstructural features, was applied to the electron micrographs over the range of pressure. Features measured were the length, breadth, and orientation of the domains, and of the voids between the domains, the domain packing density, and some aspects of inter-domain contacts. The fabric changes accompanying consolidation are described. The void ratio curve exhibited two stages of consolidation, the change occurring at a pressure of approximately 0·15 kg/cm2 (14·7 kN/m2). Many of the measured features showed similar patterns of variation. This is attributed to the rupture of inter-domain (and inter-particle) physico-chemical bonds at about this pressure. On a consolidé des échantillons de kaolin remaniés, sous différenes pressions allant jusqua'à 1000 kg/cm2 (100 000 kN/m2). On a préparé et examiné ces échantillons au microscope électronique et on a utilisé une nouvelle méthoded'analyse quantitative, mettant en jeu la mesure directe des microstructures pour l'étude des microphotographies électroniques couvrant le domaine de pression étudié. Les caractéristiques mesurées sont: la longueur, la largeur et l'orientation des particules, et des vides entre et l'orientation des particules, et des vides entre les domaines, la densité d'empilemet des particules, et quelques autres aspects des contacts entre les particules. On décrit les changemet de structure qui se produisent par consolidation. La courbe de l'indice des vides démontre qu'il y a deux étapes dans la consolidation, le changement se produisant à une pression d'environ 0·15kg/cm2 (14·7 kN/m2). Un grand nombre de caractéristiques structurales suivent un schéma de variation similaire. On attribue ceci à la rupture des liaisons physicochimiques entre particules autour de cette pression.

This publication has 0 references indexed in Scilit: