Concerning the mechanism of transcrystalline stress-corrosion cracking of α-brass
- 1 April 1984
- journal article
- Published by Elsevier in Scripta Metallurgica
- Vol. 18 (4) , 321-326
- https://doi.org/10.1016/0036-9748(84)90445-9
Abstract
No abstract availableThis publication has 11 references indexed in Scilit:
- Correlation of acoustic and electrochemical noise in the stress-corrosion cracking of α-brassScripta Metallurgica, 1983
- Stress corrosion of Cu- Zn and Cu- Zn- Ni alloys: The role of dealloyingMetallurgical Transactions A, 1982
- Liquid-metal embrittlement in an Al 6%Zn3%Mg alloyActa Metallurgica, 1981
- The propagation of transgranular stress-corrosion cracks in admiralty metalMetallurgical Transactions A, 1980
- Fractographic aspects of the stress corrosion cracking of α-brass in 15N ammonia solutionsCorrosion Science, 1979
- Hydrogen embrittlement and liquid-metal embrittlement in nickel single crystalsScripta Metallurgica, 1979
- Brittle fracture in iridiumMetallurgical Transactions A, 1978
- Stress Corrosion Cracking of Admiralty Brass in Aqueous Copper SulfateCorrosion, 1976
- Critical Potentials for Stress Corrosion Cracking of 63‐37 Brass in Ammoniacal and Tartrate SolutionsJournal of the Electrochemical Society, 1975
- Some observations on the stress-corrosion cracking of α-brass and similar alloysPhilosophical Magazine, 1960