Fatigue crack acceleration and closure in rotating bending tests of 0.54% carbon steel
- 31 December 1978
- journal article
- Published by Elsevier in Engineering Fracture Mechanics
- Vol. 10 (4) , 855-866
- https://doi.org/10.1016/0013-7944(78)90039-5
Abstract
No abstract availableKeywords
This publication has 19 references indexed in Scilit:
- Fatigue crack closure under cyclic tensionPublished by Elsevier ,2003
- Observation of crack-closure behavior after single overload cycles in 7075-T6 single-edge-notched specimensEngineering Fracture Mechanics, 1977
- Successive Observations of Crack Closure Behavior at the Tip of Fatigue CrackJournal of the Society of Materials Science, Japan, 1974
- Crack growth retardation under aircraft spectrum loadsEngineering Fracture Mechanics, 1973
- Fatigue crack closure at positive stressesEngineering Fracture Mechanics, 1972
- Spectrum Loading and Crack GrowthJournal of Basic Engineering, 1972
- Fatigue Crack Propagation in Low-Carbon Steel under Doubly-Repeated StressJournal of the Society of Materials Science, Japan, 1972
- Service Load and Fatigue Strength : Report 12 Crack Propagation of Small Size and Middle Size Test PiecesTransactions of the Japan Society of Mechanical Engineers, 1969
- Service Load and Fatigue Strength : Report 8, Crack propagation of Medium Carbon Steel under Two-Fold Multiple Repeated Stress in Tow-Stress Levels and Three-Fold Multiple Repeated Stress in Three-Stress LevelsTransactions of the Japan Society of Mechanical Engineers, 1968
- Fatigue Strength and Deformation at Rotating Bending in Program Loading TestsJournal of the Society of Materials Science, Japan, 1968