Growth of Defect Clusters in Thin Nickel Foils during Electron Irradiation. II. Temperature Dependence of the Growth Rate of Interstitial Loops
- 16 July 1971
- journal article
- research article
- Published by Wiley in Physica Status Solidi (a)
- Vol. 6 (1) , 173-185
- https://doi.org/10.1002/pssa.2210060120
Abstract
No abstract availableKeywords
This publication has 14 references indexed in Scilit:
- Growth of defect clusters in thin nickel foils during electron irradiation (I)Physica Status Solidi (a), 1971
- The growth of voids in nickel in a high-voltage electron microscopePhilosophical Magazine, 1971
- Vacancy tetrahedra in copper due to electron irradiation in the high-voltage microscopePhilosophical Magazine, 1970
- Dislocation loop growth in an electron irradiated thin foilPhilosophical Magazine, 1970
- Voids in nickel after electron irradiationPhysica Status Solidi (a), 1970
- Voids in Nickel irradiated with Electrons after Previous Argon Ion BombardmentNature, 1970
- The Separability of the Diffusion Equation with Drift TermPhysica Status Solidi (b), 1970
- Electron displacement damage in copper and aluminium in a high voltage electron microscopePhilosophical Magazine, 1968
- Theoretical Treatment of the Kinetics of Diffusion-Limited ReactionsPhysical Review B, 1957
- Diffusion-Limited Annealing of Radiation Damage in GermaniumPhysical Review B, 1957