Synthesis of LiMnO2 with α ‐ NaMnO2‐Type Structure by a Mixed‐Alkaline Hydrothermal Reaction

Publisher Website
Google Scholar
Abstract
A metastable form of with ‐type structure (layered‐ ) was synthesized directly from by hydrothermal reaction at 220°C using aqueous mixed‐alkaline solutions such as or LiCl‐KOH. Relatively highly crystallized samples could be obtained by a one‐step process, compared with that of an ion‐exchanged sample obtained previously. Magnetization data between 83 and 500 K show that manganese ions are present as 3+ in high‐spin state and a broad maximum is observed ca. 250 K, suggesting a yield of antiferromagnetic ordering below room temperature. Preliminary electrochemical tests using coin‐type cells in which lithium metal was used as negative electrode material show that about 100 mAh/g specific capacity remained at the eighth cycle between 2.0 and 4.3 V, whereas the initial charge capacity reached ca. 210 mAh/g up to 4.3 V.