Micro‐Raman and IR study of the compressive behaviour of poly(paraphenylene benzobisoxazole) (PBO) fibres in a diamond‐anvil cell

Publisher Website
Google Scholar
Abstract
The micro/nano structural evolution of PBO (poly(paraphenylenebenzobisoxazole), commercial name Zylon) fibres has been studied by Raman and IR spectroscopy in a diamond‐anvil cell, up to ∼15 GPa. Different modes were considered in the 900–1700 cm−1 (Raman) and 800–3300 cm−1 (IR) spectral range. The material behaviour appears more similar to that of a densely packed inorganic structure than to the behaviour previously observed for polyamide fibres, and is related to the compact arrangement of the rigid heterocyclic rings. Wavenumber shift starts with increase in pressure and a transition between the two regimes was revealed at ∼2–2.5 GPa, and it was assigned to the loss of order between neighbouring PBO chains. A good correlation is observed between the macroscopic mechanical properties and the nanomechanics at the chemical bond scale. Copyright © 2006 John Wiley & Sons, Ltd.