Calculated grain size-dependent vacancy supersaturation and its effect on void formation
- 1 April 1974
- journal article
- research article
- Published by Taylor & Francis in Philosophical Magazine
- Vol. 29 (4) , 847-858
- https://doi.org/10.1080/14786437408222075
Abstract
In order to study the effect of grain size on void formation during high-energy electron irradiations, the steady-state point defect concentration and vacancy supersaturation profiles have been calculated for three-dimensional spherical grains up to three microns in size. In the calculations of vacancy supersaturation as a function of grain size, the effects of internal sink density and the dislocation preference for interstitial attraction have been included. The computations show that the level of vacancy supersaturation achieved in a grain decreases with decreasing grain size. The grain size dependence of the maximum vacancy supersaturation in the centre of the grains is found to be very similar to the grain size dependence of the maximum void number density and void volume swelling measured in the central regions of austenitic stainless steel grains. This agreement reinforces the interpretation that the grain size effect is due primarily to the depletion of point defects from the grain interior. It is suggested that the void nucleation is strongly dependent on the level of vacancy supersaturation.Keywords
This publication has 6 references indexed in Scilit:
- The role of vacancies and dislocations in the nucleation and growth of gas bubbles in irradiated fissile materialPublished by Elsevier ,2003
- Effect of grain size on void formation during high-energy electron irradiation of austenitic stainless steelPhilosophical Magazine, 1974
- Inhibited void formation in dispersion-hardened austenitic stainless steel during high-energy electron irradiationJournal of Nuclear Materials, 1973
- The diffusion of point defects to the foil surface during irradiation damage experiments in the high voltage electron microscopeRadiation Effects, 1972
- Voids in irradiated metals (Part I)Radiation Effects, 1972
- Radiation Enhanced Diffusion in SolidsJournal of Applied Physics, 1958