An experimental study of the mobility of edge dislocations in pure copper single crystals
- 1 June 1970
- journal article
- research article
- Published by Taylor & Francis in Philosophical Magazine
- Vol. 21 (174) , 1147-1168
- https://doi.org/10.1080/14786437008238500
Abstract
The velocity of edge dislocations in 99.999% pure copper crystals has been measured as a function of stress at temperatures from 66°K to 373°K by means of a torsion technique. The range of resolved shear stress was 0 to 15 megadynes/cm2 for seven temperatures (66°K, 74°K, 83°K, 123°K, 173°K, 296°K, 373°K). Dislocation mobility is characterized by two distinct features : (a) relatively high velocity at low stress (maximum velocities of about 9000 cm/see were realized at low temperatures), and (b) increasing velocity with clecreasing temperature at constant stress. The relation between dislocation velocity and resolved shear stress is: where v is the dislocation velocity at resolved shear stress τ, v o is a constant velocity chosen equal to 2000 cm/sec, τ0 is the resolved shear stress required to maintain velocity v 0, and n is the mobility coefficient. The experimental results indicate that τ0 decreases from 16.3 × 106 to 3.3 × 106 dynes/cm2 and n increases from about 0.9 to 1.1 as the temperature is lowered from 296°K to 66°K. The experimental dislocation behaviour is qualitatively consistent with an interpretation on the basis of phonon drag.Keywords
This publication has 24 references indexed in Scilit:
- Experimental techniques for observing dislocations by the Berg–Barrett methodActa Crystallographica Section A, 1968
- Damping of Dislocations in Lead Single CrystalsJournal of Applied Physics, 1967
- Machine for Producing Square Torsion Pulses of Microsecond DurationReview of Scientific Instruments, 1964
- Ultrasonic-Wave Propagation in Pure Silicon and GermaniumThe Journal of the Acoustical Society of America, 1964
- The [111] Dislocation in a Cubic CrystalPhysica Status Solidi (b), 1964
- Phonon Viscosity and Its Effect on Acoustic Wave Attenuation and Dislocation MotionThe Journal of the Acoustical Society of America, 1960
- Influence of Elastic Anisotropy on the Dislocation Contribution to the Elastic ConstantsPhysical Review B, 1959
- Theory of Mechanical Damping Due to DislocationsJournal of Applied Physics, 1956
- Thermoelasticity and Irreversible ThermodynamicsJournal of Applied Physics, 1956
- Über den Einfluß thermisch angeregter Schallwellen auf die plastische DeformationThe European Physical Journal A, 1950