PREPARATION AND CHARACTERIZATION OF SULFONATED POLYSTYRENE LATEXES

Publisher Website
Google Scholar
Abstract
The purpose of the work was the preparation of aqueous suspensions of model spherical particles stabilized by ionizable groups covalently bound to the surface. Starting material.was a 80/20 styrene/divinylbenzene latex. The latex had an average particle diameter of 500 Å as determined in the electron microscope. The copolymer was sulfonated in dichloroethane with a 3/1 SO3/triethylphosphate complex in a concurrent-flow fast-reaction apparatus and was purified by dialysis and ion exchange.Three main fractions with neutralization equivalents, Ne of 0.9, 1.8, and 2.7 meq g−1 were prepared. Elemental analysis revealed that the varying Ne in these fractions resulted from the absorption of Ca2+ and Mg2+ ions which were tightly bound to the inner-lying sulfonic groups of the particles. Treatment with strong acid followed by ion exchange eliminated the bivalent ions and increased Ne, but the titration pattern was markedly changed after such treatment. Sulfonation caused both the partial specific volume and the refractive index increment to decrease. Electron micrographs showed that the latex particles were only slightly polydisperse and that there was little change in size and shape after sulfonation. Light-scattering measurements established the absence of aggregates in the sulfonated latex. Particle sizes, determined from the intrinsic viscosities, indicated some swelling of the particles in 1 M aqueous NaCl. The extent to which the sulfonated latex satisfies the criteria required of a model colloid to be used for a study of electroviscous behavior is discussed.

This publication has 29 references indexed in Scilit: