Thermal Conductivity and Far-Infrared Absorption of UO2

Publisher Website
Google Scholar
Abstract
The thermal conductivity of single‐crystal UO2 has been measured from liquid‐helium temperature up to room temperature. The sample temperature was determined, with a helium gas bulb thermometer, and the temperature gradient was measured with Au–Co vs Manganin differential thermo‐couples. In the vicinity of the Néel temperature, TN=30.8°K, the conductivity is depressed by two orders of magnitude, from that expected for a similar diamagnetic crystal. The experimental results demonstrate that a strong phonon‐magnon coupling exists in this crystal. The far‐infrared transmission of the same UO2 crystal has been measured from a frequency of 5–115 cm−1 at 3°K. A grating monochromator and a Strong‐type lamellar interferometer have been used for these measurements. A sharp absorption line has been found at 17.63±0.1 cm−1. Broader absorption lines have been observed at 19.2, 23, 79, and 100 cm−1. Transmission measurements in which a 50‐kG magnetic field is applied to the sample or the sample temperature is varied indicate that impurity‐induced absorptions occur at 19.2 and 23 cm−1, and the three remaining lines can be identified with the antiferromagnetic state of UO2.