Mechanisms of environmentally assisted cracking in AlZnMg single crystals
- 1 January 1982
- journal article
- Published by Elsevier in Corrosion Science
- Vol. 22 (10) , 925-937
- https://doi.org/10.1016/0010-938x(82)90062-2
Abstract
No abstract availableThis publication has 21 references indexed in Scilit:
- Fracture mechanics and surface chemistry studies of fatigue crack growth in an aluminum alloyMetallurgical Transactions A, 1980
- Discontinuous propagation of stress corrosion cracks in AlZnMg alloysScripta Metallurgica, 1979
- Hydrogen Induced Fracture of a High Strength Aluminum AlloyCorrosion, 1979
- Hydrogen embrittlement of a cyclically deformed high strength Al alloyMetallurgical Transactions A, 1977
- Pre-exposure embrittlement and stress corrosion failure in AlZnMg AlloysCorrosion Science, 1976
- The occurrence of trcmsgranular cleavage-like fracture in an Al-Zn-Mg alloy during tensile testingMetallurgical Transactions A, 1975
- Embrittlement by liquid metalsProgress in Materials Science, 1973
- Effect of cyclic stress wave form on corrosion fatigue crack propagation in al-zn-mg alloysMetallurgical Transactions, 1972
- Crack propagation in a liquid metal environmentActa Metallurgica, 1963
- On a surface energy mechanism for stress-corrosion crackingActa Metallurgica, 1961