A physicochemical study of the morphology of progesterone‐loaded microspheres fabricated from poly(D,L‐lactide‐co‐glycolide)

Publisher Website
Google Scholar
Abstract
Progesterone-loaded microspheres are fabricated by a solvent evaporation process from a poly(D,L-lactide-co-glycolide) (85/15 PLG) and from α-progesterone. Methylene chloride is used as solvent and polyvinyl alcohol and methylcellulose are used as surfactants. The microspheres are characterized by scanning electron microscopy, differential scanning calorimetry, and x-ray powder diagrams. Our study shows that the morphology and the thermal behavior of PLG microspheres can vary significantly with progesterone loading and sample thermal history. Below and at 16.5% loading the microspheres exhibit a smooth outer surface. Above 23% loading, the surface becomes rough, embedded by copolymer particles or well-defined crystals. Pores and cracks can also be observed. Below 35% the progesterone is molecularly dispersed. At 35% and above crystal doMayns of the steroid appear and two crystalline forms are found: α- and β-progesterone. The physical state of progesterone and the nature of its crystal doMayns dispersed in the PLG matrix can change during storage. Also a progressive development of an endothermic peak at the Tg event of the copolymer is observed during storage. No well defined relationship of peak size to progesterone loading can be shown.

This publication has 8 references indexed in Scilit: