Effects of iodine concentration on iodine-induced stress corrosion cracking of zircaloy-4 tube
- 1 May 1988
- journal article
- Published by Elsevier in Journal of Nuclear Materials
- Vol. 152 (2-3) , 194-203
- https://doi.org/10.1016/0022-3115(88)90327-3
Abstract
No abstract availableKeywords
This publication has 14 references indexed in Scilit:
- On the initiation of cracks in Zircaloy tubes by I2 and Cs/Cd vapoursJournal of Nuclear Materials, 1986
- Thermally activated deformation of Zircaloy-4Journal of Nuclear Materials, 1984
- Elongation minimum and strain rate sensitivity minimum of zircaloy-4Journal of Nuclear Materials, 1983
- A fractographic study of iodine-induced stress corrosion cracking in irradiated Zircaloy-2 claddingJournal of Nuclear Materials, 1983
- Chemical aspects of iodine-induced stress corrosion cracking failure of zircaloy-4 tubing above 50°CJournal of Nuclear Materials, 1983
- Stress corrosion cracking of zircaloy by cadmium, iodine, and metal iodidesJournal of Nuclear Materials, 1983
- A thermodynamic assessment of in-reactor iodine scc of zircaloyJournal of Nuclear Materials, 1982
- Halogen stress corrosion cracking of zircaloy-4 tubingJournal of Nuclear Materials, 1975
- Fracture of Zircaloy cladding under simulated power ramp conditionsJournal of Nuclear Materials, 1973
- Factors affecting stress corrosion cracking of zircaloy in iodine vapourJournal of Nuclear Materials, 1972