Bulk texture and transport properties of magnetic field/liquid assisted textured YBa/sub 2/Cu/sub 3/O/sub 7-x/ tape-cast films
- 1 June 1999
- journal article
- Published by Institute of Electrical and Electronics Engineers (IEEE) in IEEE Transactions on Applied Superconductivity
- Vol. 9 (2) , 1463-1466
- https://doi.org/10.1109/77.784668
Abstract
Textured YBa/sub 2/Cu/sub 3/O/sub 7-x/ films (thickness=250 /spl mu/m) were fabricated by tape casting in an applied magnetic field (H=6 T). Platinum (1 wt.%) was incorporated to induce liquid phase-assisted densification in films fired on silver (Ag) foil to 935-942/spl deg/C under reduced pO/sub 2/(g) conditions. The transport critical current densities (J/sub ct/) of such films exhibited nearly field insensitive behavior between H=0-3 T (H/spl par/c-axis) at 77 K, with J/sub ct/>1000 A/cm/sup 2/ at H=0 T.Keywords
This publication has 19 references indexed in Scilit:
- Transport properties of magnetic field/liquid assisted textured YBa2Cu3O7−x thick filmsApplied Physics Letters, 1995
- Phase equilibria in the YBCuO system and melt processing of Ag clad Y1Ba2Cu3O7−x tapes at reduced oxygen partial pressuresPhysica C: Superconductivity and its Applications, 1995
- Platinum enhanced textured growth of grain-aligned YBa2Cu3O7−x thick filmsJournal of Applied Physics, 1994
- Platinum-enhanced densification of grain-aligned YBa2Cu3O7−x filmsApplied Physics Letters, 1994
- Continuous crystal growth of YBa2Cu3O7−x by the modified top-seeded crystal pulling methodPhysica C: Superconductivity and its Applications, 1993
- Semisolid solidification of high temperature superconducting oxidesJournal of Applied Physics, 1992
- Preparation of aligned high Tc superconducting composite tape by laser deposition process on metallic substrateCryogenics, 1991
- Critical current density enhancement in YBa2Cu3O6.8 films on buffered metallic substratesApplied Physics Letters, 1991
- Superconducting transport properties of grain boundaries in bicrystalsPhysical Review B, 1990
- Orientation Dependence of Grain-Boundary Critical Currents inBicrystalsPhysical Review Letters, 1988