Studies on Nickel Oxide Mixed Catalysts (X) Thermoanalytical Investigations on NiO/SiO2 Catalysts and Nickel Layer‐silicates

Publisher Website
Google Scholar
Abstract
The processes occurring at the thermal decomposition of NiO/SiO2 catalysts prepared by precipitation deposition of nickel talc and nickel antigorite were investigated by means of DTA/TG method, high temperature X‐ray diffraction and infrared spectroscopy. In the case of NiO/SiO2 samples X‐ray amorphous nickel layer‐silicates (mixtures of nickel antigorite/nickel talc) were formed in the process of preparation. Nickel hydroxide was observed at NiO contents > 40 mol%. Nickel talc and nickel antigorite decompose at increasing temperatures successively to the following phases: nickel talc, nickel antigorite → X‐ray amorphous phase → nickel oxide, nickel olivine, cristobalite.The dehydroxylation temperatures of the X‐ray amorphous nickel layer‐silicates are markedly lower than those of nickel talc and nickel antigorite.Es wurde die thermische Umwandlung durch Fällen hergestellter NiO/SiO2‐Katalysatoren, von Nickeltalk und von Nickelantigorit durch die Anwendung von DTA/TG‐Methoden, der Hochtemperatur‐Röntgendiffraktometrie und der Infrarotspektroskopie untersucht. Bei den NiO/SiO2‐Proben wurden im Verlaufe des Fällungsprozesses röntgenamorphe Nickelschichtsilikate (Nickeltalk/Nickelantigorit‐Gemische) gebildet. Nickelhydroxid wurde bei NiO‐Gehalten > 40 mol‐% beobachtet. Nickeltalk und Nickelantogorit zerfallen bei Temperaturerhöhung folgendermaßen: Nickeltalk, Nickelantigorit → → röntgenamorphe Phase → Nickeloxid, Nickelolivin, Cristobalit. Die Dehydroxylierungstemperaturen der röntgenamorphen Nickelschichtsilikate sind beträchtlich niedriger als die von Nickeltalk und Nickelantigorit.