Elastic biodegradable poly(glycolide‐co‐caprolactone) scaffold for tissue engineering
- 3 June 2003
- journal article
- research article
- Published by Wiley in Journal of Biomedical Materials Research Part A
- Vol. 66A (1) , 29-37
- https://doi.org/10.1002/jbm.a.10497
Abstract
Cyclic mechanical strain has been demonstrated to enhance the development and function of engineered smooth muscle (SM) tissues, and it would be necessary for the development of the elastic scaffolds if one wishes to engineer SM tissues under cyclic mechanical loading. This study reports on the development of an elastic scaffold fabricated from a biodegradable polymer. Biodegradable poly(glycolide‐co‐caprolactone) (PGCL) copolymer was synthesized from glycolide and ϵ‐caprolactone in the presence of stannous octoate as catalyst. The copolymer was characterized by 1H‐NMR, gel permeation chromatography and differential scanning calorimetry. Scaffolds for tissue engineering applications were fabricated from PGCL copolymer using the solvent‐casting and particle‐leaching technique. The PGCL scaffolds produced in this fashion had open pore structures (average pore size = 250 μm) without the usual nonporous skin layer on external surfaces. Mechanical testing revealed that PGCL scaffolds were far more elastic than poly(lactic‐co‐glycolic acid) (PLGA) scaffolds fabricated using the same method. Tensile mechanical tests indicated that PGCL scaffolds could withstand an extension of 250% without cracking, which was much higher than withstood by PLGA scaffolds (10–15%). In addition, PGCL scaffolds achieved recoveries exceeding 96% at applied extensions of up to 230%, whereas PLGA scaffolds failed (cracked) at an applied strain of 20%. Dynamic mechanical tests showed that the permanent deformation of the PGCL scaffolds in a dry condition produced was less than 4% of the applied strain, when an elongation of 20% at a frequency of 1 Hz (1 cycle per second) was applied for 6 days. Moreover, PGCL scaffolds in a buffer solution also had permanent deformations less than 5% of the applied strain when an elongation of 10% at a frequency of 1 Hz was applied for 2 days. The usefulness of the PGCL scaffolds was demonstrated by engineering SM tissues in vivo. This study shows that the elastic PGCL scaffolds produced in this study could be used to engineer SM‐containing tissues (e.g. blood vessels and bladders) in mechanically dynamic environments. © 2003 Wiley Periodicals, Inc. J Biomed Mater Res 66A: 29–37, 2003Keywords
This publication has 21 references indexed in Scilit:
- Microstructure analysis and thermal property of copolymers made of glycolide and ϵ‐caprolactone by stannous octoateJournal of Polymer Science Part A: Polymer Chemistry, 2002
- Functional Arteries Grown in VitroScience, 1999
- Cross-linking of dermal sheep collagen using a water-soluble carbodiimideBiomaterials, 1996
- Monocryl® suture, a new ultra-pliable absorbable monofilament sutureBiomaterials, 1995
- Stretch affects phenotype and proliferation of vascular smooth muscle cellsMolecular and Cellular Biochemistry, 1995
- Mechanical strain induces growth of vascular smooth muscle cells via autocrine action of PDGF.The Journal of cell biology, 1993
- Relations between in vitro cytotoxicity and crosslinked dermal sheep collagensJournal of Biomedical Materials Research, 1992
- Biochemical changes and cytotoxicity associated with the degradation of polymeric glutaraldehyde derived crosslinksJournal of Biomedical Materials Research, 1990
- Chemically modified collagen: A natural biomaterial for tissue replacementJournal of Biomedical Materials Research, 1987
- Polylactones. 1. Copolymerizations of glycolide and iε-caprolactoneMacromolecules, 1984