Corrosion Mechanisms and Products of Copper in Aqueous Solutions at Various pH Values
- 1 May 1997
- journal article
- Published by Association for Materials Protection and Performance (AMPP) in Corrosion
- Vol. 53 (5) , 389-398
- https://doi.org/10.5006/1.3280482
Abstract
The corrosion behavior of copper in aqueous solutions of different pH values was investigated using electrochemical and surface analysis methods. It was shown that the corrosion mechanism changed with pH and was associated with morphology of the surf ace films formed. In solution of pH 3, the copper surface was covered with porous corrosion products of cuprous oxide (Cu2O). Corrosion was controlled predominately by diffusion in solution. In solutions of pH 4 to pH 5, formation of cubic Cu2O on the copper surface provided a diffusion barrier to copper dissolution. The anodic process was controlled by a mixed diffusion of copper ions in oxide films and in solution. In solutions of pH 6 to pH 9, the oxide films (Cu2O) became more protective. Diffusion in the oxide films became a rate-determining step of anodic dissolution. In pH 10 solution, a thin, compact Cu2O film formed, and spontaneous passivation was observed. At pH 12 and pH 13, analysis by x-ray photoelectron spectroscopy (XPS) and scanning ...Keywords
This publication has 0 references indexed in Scilit: