Crack nucleation in hydrogen embrittlement
- 1 December 1992
- journal article
- Published by Elsevier in Scripta Metallurgica et Materialia
- Vol. 27 (12) , 1701-1705
- https://doi.org/10.1016/0956-716x(92)90005-y
Abstract
No abstract availableThis publication has 11 references indexed in Scilit:
- An environmental effect as the major cause for room-temperature embrittlement in FeAlPublished by Elsevier ,2003
- Cracking behavior of FeAl (40 at % Al) alloys during cutting operationsScripta Metallurgica et Materialia, 1992
- Environmental Embrittlement in FeAl Aluminides.ISIJ International, 1991
- Hydrogen and dislocations in high-chromium ferriteScripta Metallurgica et Materialia, 1991
- Environmental embrittlement in boron-free and boron-doped FeAl (40 at. % Al) alloysScripta Metallurgica et Materialia, 1990
- Environmental effects on room-temperature ductility and fracture in Fe3AlScripta Metallurgica et Materialia, 1990
- Mobility of 〈001〉 dislocations and formation of cleavage nucleiScripta Metallurgica et Materialia, 1990
- Chemical driving force for dislocation motion in hydrogen embrittlementScripta Metallurgica, 1986
- Hydrogen Embrittlement of SteelsAnnual Review of Materials Science, 1978
- Hydrogen embrittlement of Nb I—Macroscopic behavior at low temperaturesActa Metallurgica, 1977