OVERLOAD RETARDATION OF FATIGUE CRACK GROWTH IN A 9%Cr 1%Mo STEEL AT ELEVATED TEMPERATURES
- 1 January 1993
- journal article
- Published by Wiley in Fatigue & Fracture of Engineering Materials & Structures
- Vol. 16 (1) , 53-70
- https://doi.org/10.1111/j.1460-2695.1993.tb00070.x
Abstract
No abstract availableKeywords
This publication has 15 references indexed in Scilit:
- Effects of temperature and environment on fatigue crack growth mechanisms in a 9% Cr 1% Mo steelActa Metallurgica et Materialia, 1992
- The effect of overload cycles on fatigue crack propagation in two structural steelsEngineering Fracture Mechanics, 1988
- Effect of single overload in FCPEngineering Fracture Mechanics, 1988
- Fatigue crack closure after overloadEngineering Fracture Mechanics, 1983
- Micromechanisms of fatigue crack growth retardation following overloadsEngineering Fracture Mechanics, 1983
- Crack growth retardation due to micro-roughness: A mechanism for overload effects in fatigueScripta Metallurgica, 1982
- Crack closure and crack propagation rates in 7050 aluminumEngineering Fracture Mechanics, 1981
- Fatigue crack growth retardation behavior of in-100 at elevated temperatureEngineering Fracture Mechanics, 1979
- Delayed retardation phenomena of fatigue crack growth in various steels and alloysJournal of Materials Science, 1978
- Fatigue crack growth retardation after single-cycle peak overload in Ti-6Al-4V titanium alloyEngineering Fracture Mechanics, 1973