Structural depth profiling of iron oxide thin films using grazing incidence asymmetric Bragg x-ray diffraction
- 15 June 1989
- journal article
- Published by AIP Publishing in Journal of Applied Physics
- Vol. 65 (12) , 4763-4768
- https://doi.org/10.1063/1.343230
Abstract
X-ray depth profiling in a grazing incidence asymmetric Bragg geometry is used to obtain the depth-dependent structure of a nominally γ-Fe2O3 thin film, which was oxidized from an Fe3O4 film. As the incidence angle is varied from angles less than the critical angle for total external reflection to angles greater than the critical angle, the x-ray penetration depth increases from about 20 to several thousand angstroms. The observed diffraction originates from this region of variable depth and a structural depth profile of the thin film can be obtained by measuring the diffraction pattern as a function of incidence angle. The iron oxide film is found to have a 45-Å-thick surface layer of α-Fe2O3; beneath this layer the film is predominantly γ-Fe2O3 but also contains about 2.6 at. % α-Fe2O3. These data, together with previous chemical and magnetic data, suggest that during oxidation of the Fe3O4 film the surface layer forms by the outward diffusion of Fe ions and their subsequent oxidization to α-Fe2O3. One possible explanation of the 2.6% α-Fe2O3 in the bulk of the film is that the Fe3O4 film contains small nuclei of material that are structurally similar to α-Fe2O3. During the oxidation to form γ-Fe2O3, these then grow to form small grains of α-Fe2O3 that are observed.This publication has 12 references indexed in Scilit:
- Physical properties of spinel iron oxide thin filmsJournal of Materials Research, 1988
- X-ray depth profiling of iron oxide thin filmsJournal of Materials Research, 1988
- Analysis of cobalt-doped iron oxide thin films by synchrotron radiationThin Solid Films, 1987
- Compositional variations in doped iron oxide magnetic thin filmsJournal of Vacuum Science & Technology A, 1987
- Grazing incidence synchrotron x-ray diffraction method for analyzing thin filmsJournal of Materials Research, 1987
- X-ray characterization of surface and bulk structures of sputtered iron oxide thin filmApplied Physics Letters, 1987
- Observation of magnetic dead layers at the surface of iron oxide filmsApplied Physics Letters, 1986
- Os-doped γ-Fe2O3 thin films having high coercivity and high coercive squarenessJournal of Applied Physics, 1984
- High density recording characteristics of sputtered γ-Fe2O3 thin-film disksJournal of Applied Physics, 1982
- New preparation process for sputtered γ-Fe2O3thin film disksIEEE Transactions on Magnetics, 1980