In situ scanning auger analysis of hydrogen-induced fracture in Ti-6Al-6V-2Sn
- 1 August 1978
- journal article
- Published by Springer Nature in Metallurgical Transactions A
- Vol. 9 (8) , 1169-1172
- https://doi.org/10.1007/bf02652222
Abstract
No abstract availableThis publication has 10 references indexed in Scilit:
- Hydride habit planes in titanium-aluminum alloysMetallurgical Transactions A, 1976
- Stress, hydrogen segregation, and Fracture in α-β titanium alloysMetallurgical Transactions A, 1976
- A film-rupture model of hydrogen-induced, slow crack growth in acicular alpha-beta titaniumMetallurgical and Materials Transactions A, 1976
- Observations of an interface phase in the α/β boundaries in titanium alloysMetallurgical Transactions A, 1975
- Effect of hydrogen on fracture and inert-environment sustained load cracking resistance of α- β titanium alloysMetallurgical Transactions, 1974
- Subcritical crack growth under sustained loadMetallurgical Transactions, 1974
- A consideration of cleavage in alpha titaniumActa Metallurgica, 1973
- Hydrogen in β transformed Ti-6Al-4VMetallurgical Transactions, 1972
- Cleavage in Ti-8Al-1Mo-1V caused by hydrogen gasMetallurgical Transactions, 1972
- Effect of stress on microsegregation of hydrogen at elevated temperatures in titanium and Ti-8Al-1Mo-1VMetallurgical Transactions, 1971