Fatigue Fracture in Fibrous Polymers as a Brittle, Crack-Nucleation Process

Publisher Website
Google Scholar
Abstract
An interpretative analysis of experimental results on the failure of synthetic fibers in fatigue under cyclic tension leads to the conclusion that rupture is of a brittle nature. Although molecular rearrangement undoubtedly takes place during longitudinal fatiguing, rupture itself cannot be regarded as a viscous,laminar flow process. Failure is localized; the undamaged sections of the specimens show relatively less important effects of the fatiguing. Lifetime cannot be predicted from measurements of fiber tenacity, modulus, or rate of creep. A theory of fatigue rupture, based on the observation of cracks in specimens strained to breakage, is formulated. The treatment involves the assumption that a crack grows by a nucleation process up to a critical size. At a slightly larger size, the crack becomes unstable and propagates spontaneously, to produce rupture. The theory leads to an expression for lifetime as a function of stress that is in substantial agreement with experimental data on a number of samples.

This publication has 17 references indexed in Scilit: