Hexagonal cobalt carbide formed by carbon ion implantation
- 15 May 1991
- journal article
- Published by AIP Publishing in Journal of Applied Physics
- Vol. 69 (10) , 7342-7344
- https://doi.org/10.1063/1.347590
Abstract
Thin films of ferromagnetic metals, i.e., bcc Fe, hcp Co, and fcc Ni, were subjected to 50-keV carbon ion implantation at room temperature. At the dose of 2.5×1017 ions/cm2, the formation of hexagonal Fe3C and Ni3C phases was confirmed by transmission electron microscopy selected area electron diffraction patterns; and more interestingly a similar pattern for Co was also observed for the first time. The phase was identified as hexagonal Co3C with a=2.685 Å and c=4.335 Å based on the spacings and intensities of the diffraction rings. The carbide formation was also confirmed by Auger electron spectra. The stoichiometry of the hexagonal structure may be extended in the range of Co3–2C as estimated from the experiments performed up to the dose of 9×1017 ions/cm2.This publication has 5 references indexed in Scilit:
- Surface mechanical properties of C implanted NiJournal of Materials Research, 1988
- Metastable phase formation in ion-implanted metalsNuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms, 1985
- Ion-bombarded-assisted reaction in the GeAuGaAs systemNuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms, 1985
- Formation of compounds by metalloid ion implantation in ironNuclear Instruments and Methods in Physics Research, 1983
- CHEMICAL EFFECTS ON THE KLL AUGER ELECTRON SPECTRUM FROM SURFACE CARBONApplied Physics Letters, 1970