Neutron damage of chemical vapour deposition diamond

Publisher Website
Google Scholar
Abstract
Many of the components of particle detectors for the next generation of high energy experiments need to be extremely radiation-hard if they are to continue to function for more than a few months. For example, in the first few year's operation of the large hadron collider, we expect about 1013 neutrons cm-2 year-1 1 cm from the beam pipe, with other particles causing about ten times as much additional damage. Diamond is being considered as both a detector material and perhaps as a structural component. We report on tests of chemical vapour deposition diamond films irradiated by 6*1014 neutrons cm-2 of energy below 10 keV, plus (2.0+or-0.5)*1014 neutrons cm-2 of energy above 10 keV peaking at about 1 MeV. The diamonds were metallized with titanium-gold contacts-strips on the front and a continuous electrode on the back. The leakage current (already extremely small) decreased by factors of about 50 as a result of the irradiation, both measured between adjacent strips and through the thickness of the samples. The detection efficiency of charged particles improved by 30-40% after irradiation. In addition, natural diamonds irradiated by 4*1014 neutrons cm-2 showed very little optical absorption in the GR1 and ND1 bands (neutral and negative vacancy) corresponding to a concentration of vacancies of 4(+or-2)*1014 cm-3.