Effects of test temperature, alloy composition, and heat treatment on iodine-induced stress corrosion cracking of unirradiated zircaloy tubing
- 31 July 1980
- journal article
- Published by Elsevier in Journal of Nuclear Materials
- Vol. 91 (2-3) , 277-292
- https://doi.org/10.1016/0022-3115(80)90227-5
Abstract
No abstract availableKeywords
This publication has 8 references indexed in Scilit:
- Threshold conditions for iodine-induced stress corrosion cracking of unirradiated zircaloy-4 tubing under internal pressurizationJournal of Nuclear Materials, 1979
- Observations on Damage Accumulation during Iodine-Induced Stress Corrosion Cracking of Zircaloy CladdingNuclear Technology, 1979
- The formation of iodine-induced stress corrosion cracks in zircaloysJournal of Nuclear Materials, 1978
- On the Pellet-Cladding Interaction PhenomenonNuclear Technology, 1977
- Environmentally induced fracture of zircaloy by iodine and cesium: the effects of strain rate, localized stresses and temperatureJournal of Nuclear Materials, 1975
- Halogen stress corrosion cracking of zircaloy-4 tubingJournal of Nuclear Materials, 1975
- Fracture of Zircaloy cladding under simulated power ramp conditionsJournal of Nuclear Materials, 1973
- Factors affecting stress corrosion cracking of zircaloy in iodine vapourJournal of Nuclear Materials, 1972