Deformation mechanism in nanocrystalline Al: Partial dislocation slip
Top Cited Papers
- 28 July 2003
- journal article
- Published by AIP Publishing in Applied Physics Letters
- Vol. 83 (4) , 632-634
- https://doi.org/10.1063/1.1594836
Abstract
We report experimental observation of a deformation mechanism in nanocrystalline face-centered-cubic Al, partial dislocation emission from grain boundaries, which consequently resulted in deformation stacking faults (SFs) and twinning. These results are surprising because (1) partial dislocation emission from grain boundaries has not been experimentally observed although it has been predicted by simulations and (2) deformation stacking faults and twinning have not been reported in Al due to its high SF energy.Keywords
This publication has 16 references indexed in Scilit:
- Microsample tensile testing of nanocrystalline copperScripta Materialia, 2003
- Deformation twinning in nanocrystalline Al by molecular-dynamics simulationActa Materialia, 2002
- Deformation of electrodeposited nanocrystalline nickelActa Materialia, 2002
- Our changing natureNature Materials, 2002
- Grain Boundaries and DislocationsScience, 2002
- Atomic-Level Observation of Disclination Dipoles in Mechanically Milled, Nanocrystalline FeScience, 2002
- Paradox of Strength and Ductility in Metals Processed Bysevere Plastic DeformationJournal of Materials Research, 2002
- Length scale and time scale effects on the plastic flow of fcc metalsActa Materialia, 2001
- Length-scale effects in the nucleation of extended dislocations in nanocrystalline Al by molecular-dynamics simulationPublished by Elsevier ,2001
- Bulk nanostructured materials from severe plastic deformationProgress in Materials Science, 2000