The mechanism of caustic cracking of carbon steels—I. Influence of electrode potential and film formation
- 1 January 1973
- journal article
- Published by Elsevier in Corrosion Science
- Vol. 13 (10) , 725-738
- https://doi.org/10.1016/s0010-938x(73)80011-3
Abstract
No abstract availableKeywords
This publication has 8 references indexed in Scilit:
- Yield-assisted anodic dissolution of brasses in ammoniacal solutionsCorrosion Science, 1971
- Anodic behaviour of mild steel during yielding in nitrate solutionsCorrosion Science, 1970
- The potential/pH diagram for a copper-water-ammonia system: its significance in the stress-corrosion cracking of brass in ammoniacal solutionsElectrochimica Acta, 1970
- Stress-corrosion cracking of mild steels in sodium hydroxide solutions containing various additional substancesCorrosion Science, 1967
- Deformation of Anodic Oxide FilmsJournal of the Electrochemical Society, 1966
- The electrochemistry of the stress-corrosion cracking of alpha brassCorrosion Science, 1965
- The de‐aeration of aqueous solutionsJournal of Chemical Technology & Biotechnology, 1962
- Stress corrosion in brass considered against the background of potential/pH diagramsElectrochimica Acta, 1961