In situ investigation of the magnetization processes in amorphous glass-covered wires by ferromagnetic resonance measurements
- 15 April 1999
- journal article
- research article
- Published by AIP Publishing in Journal of Applied Physics
- Vol. 85 (8) , 5453-5455
- https://doi.org/10.1063/1.369973
Abstract
The magnetization processes in amorphous glass-covered wires with positive (Fe based), negative (Co based), and nearly zero magnetostriction (Co based with a small amount of Fe addition) are analyzed by ferromagnetic resonance (FMR) measurements. A second peak in the low field range of the derivative resonance spectra has been observed for all samples. A clear relationship between the shape of this peak and the type of magnetization process that occurs in these wires was found. The obtained results show that FMR measurements offer new possibilities of investigating the magnetization processes in amorphous glass-covered wires.This publication has 9 references indexed in Scilit:
- Ferromagnetic resonance studies of amorphous and nanocrystalline FeCuNbSiB alloysJournal of Applied Physics, 1997
- Amorphous glass-covered magnetic wires for sensing applicationsSensors and Actuators A: Physical, 1997
- Comparative study of the giant magneto-impedance effect in CoFeSiB glass-covered and cold-drawn amorphous wiresIEEE Transactions on Magnetics, 1997
- Resonant microwave cavity response of amorphous ribbonsJournal of Applied Physics, 1996
- Amorphous glass-covered magnetic wires: Preparation, properties, applicationsProgress in Materials Science, 1996
- Magnetic behavior of negative and nearly zero magnetostrictive glass-covered amorphous wiresIEEE Transactions on Magnetics, 1996
- Magnetization of thin films with in-plane uniaxial anisotropy studied by microwave absorptionJournal of Applied Physics, 1995
- Linear and nonlinear spin wave resonances in a very thin amorphous wireJournal of Magnetism and Magnetic Materials, 1984
- Ferromagnetic resonance in amorphous (FeNi)80P10B10 alloys I. Alloys with high curie temperaturePhysica Status Solidi (a), 1981