Effect of crack initiation mode on low cycle fatigue life of type 304 stainless steel with surface roughness
- 31 December 1990
- journal article
- Published by Elsevier in Materials Letters
- Vol. 10 (6) , 223-230
- https://doi.org/10.1016/0167-577x(90)90022-e
Abstract
No abstract availableKeywords
This publication has 15 references indexed in Scilit:
- Effect of surface roughness on low-cycle fatigue life of CrMoV steel at 550 °CInternational Journal of Fatigue, 1989
- Surface intergranular cracking in large strain fatigueActa Metallurgica, 1987
- On the failure condition in strain-controlled low cycle fatigueInternational Journal of Fatigue, 1985
- SOME CREEP/FATIGUE PROPERTIES OF TYPE 316 STEEL AT 625°CFatigue & Fracture of Engineering Materials & Structures, 1980
- The role of cyclic hardening in crack nucleation at high strain amplitudeMaterials Science and Engineering, 1978
- Substructural development during low cycle fatigue of AISI 304 stainless steel at 649°CActa Metallurgica, 1977
- Effect of surface roughness on low-cycle fatigue behavior of type 304 stainless steelMetallurgical Transactions A, 1975
- The influence of grain boundaries on mechanical propertiesMetallurgical Transactions, 1972
- Initial stages of damage in high stress fatigue in some pure metalsPhilosophical Magazine, 1963
- Fatigue damage and crack growth in aluminium alloysActa Metallurgica, 1963