Phase Equilibria in the System CaO‐MgO‐Iron Oxide at 1500°C
- 1 July 1965
- journal article
- Published by Wiley in Journal of the American Ceramic Society
- Vol. 48 (7) , 359-364
- https://doi.org/10.1111/j.1151-2916.1965.tb14761.x
Abstract
Phase relations in the system CaO‐MgO‐iron oxide were determined at 1500°C at two levels of oxygen pressure, 10–9 atm and 0.2 atm (air). Particular attention was directed toward de termining the maximum amount of iron oxide which may be tolerated in CaO‐MgO‐iron oxide bodies before a liquid phase forms under equilib rium conditions at the two chosen oxygen pres sures. Inferences are made regarding the possible bearing of the results on the perform ance of tar‐bonded dolomite brick used in steel making furnaces.Keywords
This publication has 8 references indexed in Scilit:
- Phase Equilibria in the System CaO-MgOJournal of the American Ceramic Society, 1963
- Das System Eisen(II)-oxyd-Magnesiumoxyd und seine Verteilungsgleichgewichte mit flüssigem Eisen bei 1520 bis 1750 °CArchiv für das Eisenhüttenwesen, 1961
- Melting Relations of Magnesium Oxide‐Iron Oxide Mixtures in AirJournal of the American Ceramic Society, 1961
- Phase Equilibria in the System CaO‐Iron Oxide in Air and at 1 Atm. O2 PressureJournal of the American Ceramic Society, 1958
- The System Iron-Oxygen. I. The Wüstite Field and Related EquilibriaJournal of the American Chemical Society, 1945
- The system MgO-FeO-SiO 2American Journal of Science, 1935
- The system MgO-FeO-Fe 2 O 3 in air at one atmosphereAmerican Journal of Science, 1931
- THE TERNARY SYSTEM CaO-Al2O3-MgO.Journal of the American Chemical Society, 1916