Effect of grain size and cold work on the near threshold fatigue crack propagation rate and crack closure in iron
- 30 November 1982
- journal article
- Published by Elsevier in Scripta Metallurgica
- Vol. 16 (11) , 1249-1254
- https://doi.org/10.1016/0036-9748(82)90477-x
Abstract
No abstract availableThis publication has 8 references indexed in Scilit:
- Some considerations on fatigue crack closure at near-threshold stress intensities due to fracture surface morphologyMetallurgical Transactions A, 1982
- On crack closure in the near-threshold regionScripta Metallurgica, 1981
- Crack closure and crack propagation rates in 7050 aluminumEngineering Fracture Mechanics, 1981
- The effects of stress ratio and grain size on near-threshold fatigue crack propagation in low-carbon steelEngineering Fracture Mechanics, 1981
- Fatigue resistance of metalsMetallurgical Transactions A, 1980
- Plastic work during fatigue crack propagation in a high strength low alloy steel and in 7050 Al-AlloyEngineering Fracture Mechanics, 1977
- The condition of fatigue crack growth in mixed mode conditionEngineering Fracture Mechanics, 1975
- The effect of friction on pin jointed single edge notch fracture toughness test specimensInternational Journal of Fracture, 1968