Synthesis and third order nonlinear optics of a new soluble conjugated porphyrin polymer

Publisher Website
Google Scholar
Abstract
The synthesis of a new soluble conjugated porphyrin polymer 4 is reported. The MALDI TOF mass spectrum shows the presence of oligomers with up to 13 repeat units and GPC gives a Mn of 53 kDa. The electronic absorption spectra of this polymer exhibit an intense Q band at 800 nm in solution and 853 nm in the solid state, demonstrating a high degree of conjugation. Electroabsorption spectroscopy shows that thin films of 4 have lower resonant third order NLO susceptibility than our previous conjugated porphyrin polymer 2, whereas closed z-scan measurements indicate that the off-resonance real susceptibility, at 1064 nm, is exceptionally large for both polymers (χ(3) R = −2 × 10−16 m2 V−2). Open z-scan measurements were also made at 1064 nm, demonstrating that the two polymers exhibit similar nonlinear absorption at this wavelength (β = 1 cm GW−1 at 0.2 mM concentration).