Elevated temperature cracking of RSP aluminum alloy 8009: Characterization of the environmental influence
- 31 December 1991
- journal article
- Published by Elsevier in Scripta Metallurgica et Materialia
- Vol. 25 (12) , 2627-2632
- https://doi.org/10.1016/0956-716x(91)90129-o
Abstract
No abstract availableThis publication has 10 references indexed in Scilit:
- Ductility and dynamic strain aging in rapidly solidified aluminum alloysMetallurgical Transactions A, 1991
- Time dependent crack growth in P/M AlFeVSi at elevated temperaturesScripta Metallurgica et Materialia, 1991
- On the embrittlement of a rapidly solidified Al-Fe-V-Si alloy after high-Temperature exposureMetallurgical Transactions A, 1991
- Tensile deformation of 2618 and AlFeSiV aluminum alloys at elevated temperaturesScripta Metallurgica et Materialia, 1990
- Influence of strain rate on the fracture toughness of Al-8Fe-1V-2Si at 315°CScripta Metallurgica et Materialia, 1990
- Fatigue crack propagation in rapidly solidified aluminum alloys at 25 °C and 300 °CMetallurgical Transactions A, 1989
- Effect of strain rate on tensile ductility for a series of dispersion-strengthened aluminum-based alloysMaterials Science and Engineering: A, 1989
- Evidence of a thin sheet toughening mechanism in Al−Fe−X alloysMetallurgical Transactions A, 1989
- The role of hydrogen in corrosion fatigue of high purity Al-Zn-Mg exposed to water vaporMetallurgical Transactions A, 1988
- The embrittlement of Al-Zn-Mg and Al-Mg alloys by water vaporMetallurgical Transactions A, 1985