Annealing and Melting of Polyoxymethylene Crystals Polymerized Within Irradiated Trioxane Crystals
- 1 November 1971
- journal article
- research article
- Published by AIP Publishing in Journal of Applied Physics
- Vol. 42 (12) , 4606-4614
- https://doi.org/10.1063/1.1659829
Abstract
Morphological changes produced by the annealing and melting of the polyoxymethylene crystals that polymerize inside irradiated trioxane crystals were observed. The crystals in which the polyoxymethylene chains were oriented parallel to the threefold axis of the trioxane underwent major reorganization when held at 184°C for 30 sec. The polyoxymethylene crystals in which the chain axis was inclined at a large angle with respect to the threefold axis of the trioxane transformed and melted at temperatures approximately 5°C lower.This publication has 9 references indexed in Scilit:
- Polyoxymethlene Crystals Grown Within Irradiated Trioxane CrystalsJournal of Applied Physics, 1970
- On the formation of lamellae during annealing of extended chain crystals of radiation-polymerized trioxaneJournal of Macromolecular Science, Part B, 1969
- X-ray crystallographic study of solid-state polymerization of trioxane and tetraoxymethyleneJournal of Macromolecular Science, Part B, 1968
- Thermal Degradation Spectrum; Instrumentation to Record Thermogravimetric ResultsJournal of Macromolecular Science: Part A - Chemistry, 1968
- Oriented crystallization in polymersJournal of Macromolecular Science, Part B, 1967
- Reversible long-period change during the annealing of crystalline polymersJournal of Macromolecular Science, Part B, 1967
- Morphology of PolyoxymethyleneJournal of Macromolecular Science: Part A - Chemistry, 1967
- Lamellar Crystallization and Melting of PolyoxymethyleneJournal of Applied Physics, 1966
- On moiré patterns in the electron microscopy of polymer crystalsPhilosophical Magazine, 1964