Static-fatigue limit of ceramic materials containing small flaws
- 1 January 1986
- journal article
- Published by Elsevier in Engineering Fracture Mechanics
- Vol. 25 (4) , 483-495
- https://doi.org/10.1016/0013-7944(86)90262-6
Abstract
No abstract availableKeywords
This publication has 15 references indexed in Scilit:
- High‐Temperature Failure of Polycrystalline Alumina: II, Creep Crack Growth and BluntingJournal of the American Ceramic Society, 1984
- Some considerations regarding the creep crack growth thresholdScripta Metallurgica, 1984
- Static Fatigue Limit for Sintered Silicon Carbide at Elevated TemperaturesJournal of the American Ceramic Society, 1983
- A Method for the Determination of a Static Fatigue Limit of GlassesPhysica Status Solidi (a), 1983
- Determination of Threshold Stress Intensity for Crack Growth at High Temperature in Silicon Carbide CeramicsJournal of the American Ceramic Society, 1983
- The Dependence of Strength‐Controlling Fracture Energy on the Flaw‐Size to Grain‐Size RatioJournal of the American Ceramic Society, 1980
- Slow Crack Growth from Controlled Surface Flaws in Hot‐Pressed Si3N4Journal of the American Ceramic Society, 1978
- Static Fatigue of Si3N4Journal of the American Ceramic Society, 1978
- Crack propagation and failure prediction in silicon nitride at elevated temperaturesJournal of Materials Science, 1974
- A method for evaluating the time-dependent failure characteristics of brittle materials ? and its application to polycrystalline aluminaJournal of Materials Science, 1972