Effects of pre-existing grain boundary microvoid distributions on fracture toughness and fatigue crack growth in low alloy steel
- 1 September 1987
- journal article
- Published by Elsevier in Acta Metallurgica
- Vol. 35 (9) , 2227-2242
- https://doi.org/10.1016/0001-6160(87)90070-8
Abstract
No abstract availableKeywords
This publication has 39 references indexed in Scilit:
- Fatigue crack closure under cyclic tensionPublished by Elsevier ,2003
- The effect of pulsed irradiation on void swelling of a pure austfnitic alloyJournal of Nuclear Materials, 1984
- Plastic flow localization due to non-uniform void distributionJournal of the Mechanics and Physics of Solids, 1984
- The effect of hydrogen induced surface asperities on fatigue crack closure in ultrahigh strength steelScripta Metallurgica, 1983
- Tentative Test Procedure For Determining the Plane Strain JI-R CurveJournal of Testing and Evaluation, 1982
- On crack closure in the near-threshold regionScripta Metallurgica, 1981
- INCORPORATING THRESHOLD AND ENVIRONMENTAL EFFECTS INTO THE DAMAGE ACCUMULATION MODEL FOR FATIGUE CRACK GROWTHFatigue & Fracture of Engineering Materials & Structures, 1980
- The influence of environment and stress ratio on fatigue crack growth at near threshold stress intensities in low-alloy steelsEngineering Fracture Mechanics, 1980
- A FATIGUE CRACK CLOSURE MECHANISM IN TITANIUMFatigue & Fracture of Engineering Materials & Structures, 1979
- On the influence of state of stress on ductile failure initiation in high strength steelsEngineering Fracture Mechanics, 1977