Abstract
Dy2O3 layers have been grown on SrTiO3 by molecular beam epitaxy. X-ray and electron diffraction patterns clearly show that Dy2O3 grows epitaxially on SrTiO3 with {100} planes parallel to the substrate surface. Transmission electron microscopy reveals that the Dy2O3 film breaks up into small domains (10–40 nm). This leads to the formation of terraces which limits the structural perfection of thin overgrown DyBa2Cu3O7 by introducing steps and small misorientations (within 3°). The resulting surface corrugation does not preclude the growth of epitaxial c-axis DyBa2Cu3O7 films with a Tc0 of 86 K. Crystallographic analysis and image calculations show that the domain growth of Dy2O3 is associated with the formation of 90° rotation twins.