Influence of Anisotropy Behavior in UOE Process for X80 Micro Alloy Steel

Publisher Website
Google Scholar
Abstract
The anisotropy of tensile properties and charpy impact fracture toughness and its relationship with UOE pipe forming has been study on X80 micro alloy steel. All samples selected from 90º and 180º of pipes in transverse and longitudinal orientations after UOE forming. The steel was supplied as a hot rolled plate with accelerated cooling. Microstructure of the micro alloy steel was various combinations of acicular ferrite, granular ferrite and M/A phases. Charpy impact fracture toughness tests were carried out in -50 °C to 0 °C. Minimum and maximum yield strength appears in the 180º and 90º of pipe in longitudinal and transverse orientations respectively. Increasing in the yield strength related to minimum amount was about 5.8 % after UOE forming. Comparison between yield strength after and before forming appears increased about 6.9 % due to forming. With decreasing in the test temperature from -50 °C to 0 °C, fracture energy decrease up to 0.9 % that it’s very little and relinquishment. However for samples that fractured in the temperature of -50 °C difference between highest and lowest energy was about 5.9 %. Charpy test results appear that fine M/A phase not a major factor on decrease of upper shelf energy, if homogenize distributed in the acicular ferrite matrix.