Preparation of Ca-Doped YBaCuO Thin Films Containing 248 Phase by RF Magnetron Sputtering
- 1 August 1990
- journal article
- Published by IOP Publishing in Japanese Journal of Applied Physics
- Vol. 29 (8A) , L1439
- https://doi.org/10.1143/jjap.29.l1439
Abstract
Ca-doped YBaCuO thin films containing predominantly a 248 phase were prepared on SrTiO3(100) substrates by sputtering three Ca-doped targets at 500°C and annealing at 750°C. The as-deposited films formed at above 500°C predominantly had a 123 phase, and those at 300°C were amorphous. On the other hand, the as-deposited films obtained at 400–500°C had an unidentified major phase with a lattice spacing of 7 Å, which changed into a 248 phase by annealing, whereas the phase of amorphous films and the 123 phase did not.Keywords
This publication has 10 references indexed in Scilit:
- Synthesis of YBa2Cu4O8 Powders by Sol-Gel Method under Ambient PressureJapanese Journal of Applied Physics, 1990
- Formation of As-Grown YBaCuO Thin Films by RF Magnetron Sputtering from Three TargetsJapanese Journal of Applied Physics, 1989
- Tc increased to 90 K in YBa2Cu408 by Ca dopingNature, 1989
- Surface Morphology and Crystal Structures of As-Grown BiSrCaCuO Thin Films Prepared by RF Magnetron Sputtering from Three TargetsJapanese Journal of Applied Physics, 1989
- Synthesis of bulk superconducting YBa2Cu4O8 at one atmosphere oxygen pressureNature, 1989
- Bulk synthesis of the 81-K superconductor YBa2Cu4O8 at high oxygen pressureNature, 1988
- Preparation of Y2Ba4Cu8O20−xthin films by thermal coevaporationApplied Physics Letters, 1988
- Properties of Y-Ba-Cu-O thin films with ordered defect structure:Physical Review B, 1988
- Ordered-defect structure in epitaxialthin filmsPhysical Review B, 1988
- Observation of a halide (F/Cl) stabilized, new perovskite phase in superconducting Y2Ba5Cu7Ox filmsApplied Physics Letters, 1988