Magnetic transition and coercivity in TbMn6Sn6

Publisher Website
Google Scholar
Abstract
In the present paper, the structure and magnetic properties of TbMn6Sn6 have been investigated. TbMn6Sn6 is found to be of HfFe6Ge6-type structure (space group P6/mmm) with a=5.5461 AA, c=9.0477 AA and V=241 AA3. This compound shows ferrimagnetic behaviour with the ordering temperature Tc=421 K. A peak is also observed in the thermal magnetic curve at 330 K. Under magnetic fields of 100, 300 and 400 Oe, the magnetization values first increase with increasing temperature, next exhibit a peak and then decrease with further increase in temperature. When the applied magnetic field is sufficiently large, e.g. 1000 and 2100 Oe, the magnetization of the whole sample decreases with increasing temperature. With increasing temperature from the range 77-300 K, the coercivity first increases, next undergoes a peak at about 200 K and then decreases. At room temperature a magnetization jump is observed in the magnetization curves at a field of about 4 kOe in both the aligned and the free powder samples. This jump may be attributed to the spin-flop or metamagnetic transition. The magnetic anisotropy field at room temperature is found to be 8.33 kOe.