Influence of dislocation doping on the recovery of neutron irradiated Fe-Co and Fe-Co-2V ordered alloys

Publisher Website
Google Scholar
Abstract
Specimens of well ordered (S ⋍ 1) Fe-Co and Fe-Co-2V alloys are plastically deformed up to 4% at room temperature, then they are irradiated at liquid hydrogen temperature with fission neutrons up to an integrated dose of 7.2.1017 n/cm2 (E > 1 MeV). We have studied the influence of the precold working treatment on the recovery of radiation induced defects. Two main results are pointed out. First in the temperature range below 200 K the recovery is unchanged compared with undoped alloys, by contrast above 200 K, stage D attributed to the annealing of vacancies is split. An additional stage D' appears and it can reasonably be assigned to the elimination of remaining vacancies on super-dislocations. Des éprouvettes d'alllages bien ordonnes (S ⋍ 1) Fe-Co et Fe-Co-2V sont déformées plastiquement de 4% à la température ambiante, elles sont ensuite irradiées aux neutrons á la température de l'hydrogene liquide à un flux intégré de 7,2.1017 n/cm2 (E > 1 MeV). Nous avons étudie l'influence de l'écrouissage sur le recuit des défauts produits par irradiation. Deux résultats principaux sont mis en évidence. Tout d'abord dans le domaine de températures inférieures à 200 K la restauration n'est pas modifiee par comparaison aux měmes alliages non écrouis, par contre au-dessus de 200 K, le strade D attribuè au recuit des lacunes se dedouble. Un stade additionnel D' apparaǐt et on peut raisonnablement I'attribuer à I'élimination des lacunes restant sur les superdislocations.